mold crack
英 [məʊld kræk]
美 [moʊld kræk]
网络 模裂
双语例句
- Analyzed the crack appearance of the cable clamp, amend unreasonable of mold gate, and solved the crack problem.
对电缆夹使用过程中断裂现象进行了分析，对模具浇口进行了改进，最终解决了问题。 - Analyze the main cause of crack of the mold plate for various kind of plastics injection molding machines, introduce how to choose your machine and what you can do in preventing the crack occurred during operation.
分析各种注塑机模板断裂的主要原因，介绍如何选用注塑机，以及在使用时如何防止注塑机模板的断裂。 - Influence of mold wear on internal crack formation in continuous casting of steel billets
结晶器磨损对连铸小方坯内裂纹形成影响的研究 - This paper studies the influence of the change of flow direction of cooling water at the botton of ingot mold and the mold material on the crack and the inner surface roughness of the ingot mold.
对锌锭模制造经过多次的改进试验，主要改进了锌锭模下端面的冷却水流向和材质，研究其对锌锭模的断裂、内腔表面粗糙度的影响； - Using temperature, mold level, mold powder, steel grades, and carbon content, sulfur content and phosphorus content of liquid steel, it predicts the surface crack of the casting slab.
运用热电偶温度数据，结合结晶器液面、保护渣、钢号、钢液C、S、P含量等数据用于板坯表面裂纹预报。 - These results verify that the severe mold wear is one of the most important reasons that induce the internal crack and even the breakout at the off-corner of billet.
从而验证了严重的结晶器磨损是连铸坯产生偏角区内裂纹乃至漏钢事故的重要原因之一。 - Due to the mold used in carrying aluminum ingots in the hot and cold working environment long time, because of the fatigue in the mold surface, which arises inevitably the crack, even rift.
由于承载铝锭的铸模长期处于冷热变化剧烈的工作环境，铸模壳体难免会因为疲劳而产生裂纹，甚至裂缝。 - It has been confirmed that change the heat-transfer character of mold flux through changing its chemical composition is very effective, and that will reduce the longitudinal crack of cracking sensitivity steel.
通过调整保护渣的化学成分来改变保护渣的传热特性，从而减少裂纹敏感性钢种的纵裂纹被证实十分有效。 - Thermal fatigue is the most common failure mode of mould, especially for large ingot mold. At present, failure hot work moulds because of thermal fatigue crack account of 70% in total failure molds in our country.
热疲劳是模具最常见的失效形式，对于大锭铸模尤其如此，目前我国热作模具因热疲劳裂纹而失效的占模具失效总数的70%左右。 - Thermal fatigue not only shortened the mold life, but also reduced production efficiency because the metal liquid entered thermal crack which lead to difficult mold unloading. Thermal fatigue also reduced the surface quality of casting.
热疲劳不仅缩短了模具寿命，也使液态金属进入热裂纹导致取件困难，降低生产效率，而且还降低了铸件表面质量。